We find that during mechanical deformation, electropulsing enhances cross-slip, producing a wavy dislocation morphology, and enhances twinning, which is similar to exactly what takes place during cryogenic deformation. For that reason, dislocations are prevented from localizing into planar slip bands that could lead towards the early failure of this alloy under tension. Our results prove that this macroscopic electroplastic behaviour comes from defect-level microstructural reconfigurat