The potentiodynamic polarization curves were plotted for both the substrate and clad samples at 0, 18, 42 and 70 h for revealing the corrosion resistance behavior. In addition, the EIS analysis was carried out to further confirm the resistance offered by the samples. The surface roughness morphology was evaluated after the corrosion process using the laser microscope, and the roughness values were measured and compared with the substrate samples. The result showed that the cladded samples experience greater hardness, lower values of su