cyclically loaded to failure or 1 million cycles, were placed in an in vitro calcification solution. MicroCT and SEM analysis showed that localised calcification levels varied spatially according to damage, where ruptured fibres offered additional calcium binding sites. Furthermore, specimens with a statistically significant lower fatigue life were associated with statistically significant higher calcification. This study revealed that mechanical damage drives calcification of GLBP. Non-destructive pre-screening of collagen fibres d