On the other hand, the excitation band at about 400 nm due to the 4f-5d transitions of Eu2+ was also detected in the excitation spectrum of Sr8MgCe(PO4)7Eu2+, and this matches well with the NUV LED chips. Moreover, the energy transfer between Eu2+ ions at different crystallographic sites was demonstrated by time-resolved photoluminescence (TRPL) spectra. A white LED with a CRI (Ra) of 82.88 and a CCT of 4238 K was prepared through a 400 nm NUV LED chip, Sr8MgCe(PO4)7Eu2+ and BaMgAl10O17Eu2+ (BAMEu2+). These results pave the way for designing better Eu2+-dop