In this study, to control the formation of non-uniformly distributed large voids and Cu-Sn alloy agglomeration, which leads to local compositional misfit and secondary phase formation, a SnS compound precursor was applied instead of metal Sn to avoid compositional non-uniformity. Using a Cu/Zn/SnS stacked precursor, a temperature tracking experiment was conducted to confirm the formation controllability of the void and the secondary phase. According to the results of this temperature-profile tracking experiment, it was confirmed that th