The paste was applied using a high-efficiency printing technique. The printed electrodes were cured in a thermal oven. For higher conductivity, photonic-sintering was carried out during post-processing. As a result, 1.1117×106 (S/m) had excellent conductivity, performed well in repeated tensile-durability experiments of 30% to 100 times, and produced a bow-tie antenna for the above electrodes. As a result of tensing up to 35% through a Network-Analyzer, there was no performance change in the resonance-frequency or return-loss value